API Exam API-580 Topic 1 Question 90 Discussion

Actual exam question for API's API-580 exam
Question #: 90
Topic #: 1
[All API-580 Questions]

Aqueous chloride solution is carried into a sensitized stainless steel vessel, the following cracking mechanism takes very rapidly depending on temperature.

Show Suggested Answer Hide Answer
Suggested Answer: C

by Karan at Jul 04, 2024, 09:50 PM

Limited Time Offer

25%

Off

Get Premium API-580 Questions as Interactive Web-Based Practice Test or PDF

Contribute your Thoughts:

Submit Cancel
Inocencia
4 months ago
Chloride stress corrosion cracking, no doubt about it. Although, if I had a nickel for every time I saw that on an exam, I'd have enough to buy the entire stainless steel industry a round of drinks.
upvoted 0 times
Yuriko
3 months ago
A: I agree, it's a common issue that can lead to some major problems if not addressed properly.
upvoted 0 times
...
Tiffiny
3 months ago
B: Yeah, it's definitely something to watch out for when dealing with stainless steel vessels.
upvoted 0 times
...
Tresa
3 months ago
A: Chloride stress corrosion cracking is no joke, it can cause serious damage.
upvoted 0 times
...
...
Ryan
4 months ago
Leak can occur? Really? That's like saying 'water is wet' as an answer choice. I'm starting to doubt the competence of the exam writer here.
upvoted 0 times
...
Maurine
4 months ago
Chloride stress corrosion cracking for sure. I'd recognize that one anywhere, even with my eyes closed. Or maybe I'd just have to sniff the solution. Mmm, the sweet smell of chloride...
upvoted 0 times
...
Alfreda
4 months ago
Sulphide stress corrosion cracking? Are you kidding me? This is clearly a chloride issue. I hope the exam doesn't get any more 'basic' than this.
upvoted 0 times
Judy
3 months ago
Let's make sure to keep an eye out for any signs of cracking in the stainless steel vessel.
upvoted 0 times
...
Malcolm
3 months ago
Yes, but in this case, with the aqueous chloride solution, chloride stress corrosion cracking is more likely.
upvoted 0 times
...
Delfina
4 months ago
Sulphide stress corrosion cracking can also be a problem in certain conditions.
upvoted 0 times
...
Curt
4 months ago
I agree, chloride stress corrosion cracking is the main concern here.
upvoted 0 times
...
...
Felicitas
5 months ago
I think leak can occur as well, so maybe B) is also a valid answer.
upvoted 0 times
...
Shaunna
5 months ago
Leak can occur? What is this, a multiple-choice quiz for toddlers? C'mon, we're professionals here.
upvoted 0 times
...
Taryn
5 months ago
Chloride stress corrosion cracking, definitely. I've seen this happen way too many times in the lab.
upvoted 0 times
Selma
4 months ago
Sulphide stress corrosion cracking is also something to watch out for in similar situations.
upvoted 0 times
...
Emmett
4 months ago
I agree, temperature plays a big role in how quickly the cracking can occur.
upvoted 0 times
...
Hoa
4 months ago
It's important to be careful with the type of solutions we use in those vessels to prevent cracking.
upvoted 0 times
...
Gretchen
5 months ago
Yes, chloride stress corrosion cracking is a common issue with stainless steel vessels.
upvoted 0 times
...
...
Eileen
5 months ago
I'm not sure, but I think A) Sulphide stress corrosion cracking could also be a possibility.
upvoted 0 times
...
Tomoko
5 months ago
I agree with Lashaunda, chloride stress corrosion cracking makes sense in this scenario.
upvoted 0 times
...
Lashaunda
6 months ago
I think the answer is C) Chloride stress corrosion cracking.
upvoted 0 times
...

Save Cancel
az-700  pass4success  az-104  200-301  200-201  cissp  350-401  350-201  350-501  350-601  350-801  350-901  az-720  az-305  pl-300  

Warning: Cannot modify header information - headers already sent by (output started at /pass.php:70) in /pass.php on line 77